BS EN 10083-3-2006 淬硬钢和回火钢.第3部分硼钢的供货技术条件.pdf
《BS EN 10083-3-2006 淬硬钢和回火钢.第3部分硼钢的供货技术条件.pdf》由会员分享,可在线阅读,更多相关《BS EN 10083-3-2006 淬硬钢和回火钢.第3部分硼钢的供货技术条件.pdf(58页珍藏版)》请在三一文库上搜索。
1、BRITISH STANDARD BS EN 10083-3:2006 Steels for quenching and tempering Part 3: Technical delivery conditions for alloy steels The European Standard EN 10083-3:2006 has the status of a British Standard ICS 77.140.10 BS EN 10083-3:2006 This British Standard was published under the authority of the Sta
2、ndards Policy and Strategy Committee on 31 August 2006 BSI 2006 ISBN 0 580 49097 1 National foreword This British Standard is the official English language version of EN 10083-3:2006. It supersedes BS EN 10083-3:1996 which is withdrawn. The UK participation in its preparation was entrusted to Techni
3、cal Committee ISE/31, Wrought steels, which has the responsibility to: A list of organizations represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which implement international or European publications referred to in this document may be
4、found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all the necessary provisions of a contract. Users are r
5、esponsible for its correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and ke
6、ep UK interests informed; monitor related international and European developments and promulgate them in the UK. Summary of pages This document comprises a front cover, an inside front cover, the EN title page, pages 2 to 54, an inside back cover and a back cover. The BSI copyright notice displayed
7、in this document indicates when the document was last issued. Amendments issued since publication Amd. No. DateComments W - - - - - - - - - - - - - 7- $- - $ 1,00 1,70 0,05 P 0,025 + 0,005 S 0,040 + 0,005b Cr 2,00 0,05 2,00 2,20 0,10 Mo 0,30 0,03 0,30 0,60 0,04 Ni 2,00 0,05 2,00 4,3 0,07 V 0,25 0,02
8、 B 0,0050 0,0003 a means that in one cast, the deviation may occur over the upper value or under the lower value of the specified range in Table 3, but not both at the same time. b For steels with a specified sulphur range of 0,020% to 0,040% according to cast analysis, the permissible deviation is
9、0,005%. EN 10083-3:2006 (E) 20 Table 7 Maximum hardness for products to be supplied in the “treated to improve shearability (+S)“ or “soft annealed (+A)“ condition Steel designationa Max. HBW in conditionb Name Number +S +A 38Cr2 1.7003 255 207 46Cr2 1.7006 255 223 34Cr4, 34CrS4 1.7033, 1.7037 255 2
10、23 37Cr4, 37CrS4 1.7034, 1.7038 255 235 41Cr4, 41CrS4 1.7035, 1.7039 255c 241 25CrMo4, 25CrMoS4 1.7218, 1.7213 255 212 34CrMo4, 34CrMoS4 1.7220, 1.7226 255c 223 42CrMo4, 42CrMoS4 1.7225, 1.7227 255c 241 50CrMo4 1.7228 -d 248 34CrNiMo6 1.6582 -d 248 30CrNiMo8 1.6580 -d 248 35NiCr6 1.5815 -d 223 36NiC
11、rMo16 1.6773 -d 269 39NiCrMo3 1.6510 -d 240 30NiCrMo16-6 1.6747 -d 270 51CrV4 1.8159 -d 248 20MnB5 1.5530 -e -f 30MnB5 1.5531 -e -f 38MnB5 1.5532 -e -f 27MnCrB5-2 1.7182 -e -f 33MnCrB5-2 1.7185 255 -f 39MnCrB6-2 1.7189 255 -f a The values apply also for the steel with hardenability requirements (+H-
12、, +HH- and +HL-grades) covered in Tables 5 and 6; see, however, footnote c. b The values are not applicable to slabs which have been continuously cast and not further deformed. c Depending on the chemical composition of the cast, and on the dimensions, particularly in the case of the +HH-grades, sof
13、t annealing may be necessary. d Where the shearability is of importance, this steel should be ordered in the “soft-annealed“ condition. e Shearable in the untreated condition. f Condition +A is not applicable for boron steels. EN 10083-3:2006 (E) 23 Table 9 Surface hardness of steels after flame or
14、induction hardening Steel designation Surface hardness HRC min. Name Number 46Cr2 1.7006 54 37Cr4/37CrS4 1.7034/1.7038 51 41Cr4/41CrS4 1.7035/1.7039 53 42CrMo4/42CrMo4 1.7225/1.7227 53 50CrMo4 1.7228 58 a The above values apply for the condition existing after quenching and tempering and surface har
15、dening according to the conditions given in Table 11 followed by stress relieving at 150C to 180C for about 1h, and they relate to cross-sections up to 100 mm diameter for the steels 46Cr2, 37Cr4/37CrS4 and 41Cr4/41CrS4, and up to 250 mm diameter for the steels 42CrMo4/42CrMoS4 and 50CrMo4. It shoul
16、d be noted that surface decarburization may lead to lower hardness values in the surface hardened zones. EN 10083-3:2006 (E) 27 Table 11 Heat treatment a Steel designationb Quenching c,d Quenchinge Temperingf End quench test Name Number C agent C C 38Cr2 1.7003 830 to 870 Oil or water 540 to 680 850
17、 5 46Cr2 1.7006 820 to 860 Oil or water 540 to 680 850 5 34Cr4 34CrS4 1.7033 1.7037 830 to 870 Water or oil 540 to 680 850 5 37Cr4 37CrS4 1.7034 1.7038 825 to 865 Oil or water 540 to 680 850 5 41Cr4 41CrS4 1.7035 1.7039 820 to 860 Oil or water 540 to 680 850 5 25CrMo4 25CrMoS4 1.7218 1.7213 840 to 9
18、00 Water or oil 540 to 680 850 5 34CrMo4 34CrMoS4 1.7220 1.7226 830 to 890 Oil or water 540 to 680 850 5 42CrMo4 42CrMoS4 1.7225 1.7227 820 to 880 Oil or water 540 to 680 850 5 50CrMo4 1.7228 820 to 870 Oil 540 to 680 850 5 34CrNiMo6 1.6582 830 to 860 Oil or water 540 to 660 850 5 30CrNiMo8 1.6580 8
19、30 to 860 Oil or water 540 to 660 850 5 35NiCr6 1.5815 840 to 860 Oil or water 530 to 630 850 5 36NiCrMo16 1.6773 865 to 885 Air, oil or water 550 to 650 850 5 39NiCrMo3 1.6510 830 to 850 Oil or water 550 to 650 850 5 30NiCrMo16-6 1.6747 840 to 860 Oil 540 to 630 850 5 51CrV4 1.8159 820 to 870 Oil 5
20、40 to 680 850 5 20MnB5 1.5530 880 to 920 Water 400 to 600 900 5 30MnB5 1.5531 860 to 900 Water 400 to 600 880 5 38MnB5 1.5532 840 to 880 Water or oil 400 to 600 850 5 27MnCrB5-2 1.7182 880 to 920 Water or oil 400 to 600 900 5 33MnCrB5-2 1.7185 860 to 900 Oil 400 to 600 880 5 39MnCrB6-2 1.7189 840 to
21、 880 Oil 400 to 600 850 5 a The conditions given in this table are for guidance. However, the temperatures specified for the end quench test are mandatory. b This table also applies for the various grades with specified hardenability (+H-, +HH- and +HL grades) covered in Tables 5 and 6. c The temper
22、atures at the lower end of the range are generally applicable to hardening in water and those at the upper end for hardening in oil. d Austenitizing period: at least 30 min (guide value). e When choosing the quenching agent the influence of other parameters, such as shape, dimensions and quenching t
23、emperature on properties and crack susceptibility should be taken into account. Other quenching agents such as synthetic quenchants may also be used. f Tempering period: at least 60 min (guide value). EN 10083-3:2006 (E) 28 Key X Distance from quenched end of test piece, mm Y Hardness, HRC 1 HH-grad
24、e 2 HL-grade 3 H-grade Figure 1a Scatter bands for the Rockwell - C hardness in the end quench hardenability test EN 10083-3:2006 (E) 29 Key X Distance from quenched end of test piece, mm Y Hardness, HRC 1 HH-grade 2 HL-grade 3 H-grade Figure 1b Scatter bands for the Rockwell - C hardness in the end
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- BS EN 10083-3-2006 淬硬钢和回火钢.第3部分硼钢的供货技术条件 10083 2006 淬硬钢 回火 部分 供货 技术 条件
链接地址:https://www.31doc.com/p-3645854.html