BS-2782-4-METHOD-451B-1978.pdf
《BS-2782-4-METHOD-451B-1978.pdf》由会员分享,可在线阅读,更多相关《BS-2782-4-METHOD-451B-1978.pdf(8页珍藏版)》请在三一文库上搜索。
1、BRITISH STANDARD BS 2782-4: Method 451B: 1978 Methods of testing Plastics Part 4: Chemical properties Method 451B: Determination of acetone-soluble matter in phenolic moulding materials after moulding IMPORTANT NOTE. Before reading this method it is essential to read the foreword, general introducti
2、on and instructions to BS 2782, issued separately. UDC 678.5/.8:678.01:543.832:678.632 Licensed Copy: London South Bank University, London South Bank University, Tue Dec 12 08:45:30 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 2782-4:Method 451B:1978 This British Standard, having been prepared unde
3、r the direction of the Plastics Standards Committee, was published under the authority of the Executive Board on 31 May 1978 BSI 11-1999 The following BSI references relate to the work on this standard: Committee reference PLC/17 Draft for comment 77/50307 DC ISBN 0 580 10218 1 A British Standard do
4、es not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an ins
5、ide front cover, pages i and ii, pages 1 and 2 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Amendments issued since publication Amd. No.Date of issueComments Li
6、censed Copy: London South Bank University, London South Bank University, Tue Dec 12 08:45:30 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 2782-4:Method 451B:1978 BSI 11-1999i Contents Page 0Introduction1 1Scope1 2References1 3Principle1 4Reagents1 5Apparatus1 6Preparation of test sample1 7Procedure
7、1 8Expression of results2 9Test report2 Figure 1 Extraction apparatus2 Licensed Copy: London South Bank University, London South Bank University, Tue Dec 12 08:45:30 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ii blank Licensed Copy: London South Bank University, London South Bank University, Tue Dec
8、 12 08:45:30 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 2782-4:Method 451B:1978 BSI 11-19991 0 Introduction This method, which has been prepared under the direction of the Plastics Standards Committee, is technically similar to Method 451A:1978 except that it is used for determining whether a giv
9、en phenolic moulding material can be used to produce mouldings that contain not more than a relatively small amount of acetone-soluble matter. In this method, mouldings of specified dimensions are prepared under specified conditions from the moulding material under test and the acetone-soluble matte
10、r in these mouldings is determined in accordance with method 450A. This method replaces method 401B of BS 2782:1970, which is being withdrawn. WARNING NOTE. This method does not necessarily detail all the precautions necessary to meet the requirements of the Health and Safety at Work etc. Act 1974.
11、Attention should be paid to any appropriate safety precautions, and the method should only be operated by trained personnel. 1 Scope This method specifies a gravimetric method for the determination of the amount of matter that can be extracted by acetone, at a temperature near its boiling point, fro
12、m finely ground samples of mouldings prepared from a phenolic moulding material. The test for acetone-soluble matter is one means for determining the relative degree of cure of phenolic mouldings made from a given material. The process of extraction is carried out under specified conditions for a sp
13、ecified time. Although a high proportion of soluble matter is determined, extraction is not necessarily complete. The results are only comparative, because the extracted material normally contains substances other than any undercured resin that may be present, for example lubricants, colouring matte
14、r and plasticizers. 2 References The following standards publications are referred to in this method. BS 410, Specification for test sieves. BS 509, Acetone. BS 2648, Performance requirements for electrically-heated laboratory drying ovens. BS 2071, Soxhlet extractor. BS 2782, Methods of testing pla
15、stics Foreword, general introduction and instructions:1975. 3 Principle The principle of the method is the hot extraction of acetone-soluble matter from a test portion which has been reduced to a finely divided state. This is followed by evaporation of the acetone, drying of the extract to constant
16、mass and weighing of the dried extract. 4 Reagents The following reagent is required: 4.1 Acetone, complying with the requirements of BS 509. 5 Apparatus The following apparatus is required: 5.1 Means of reducing the moulded sample to a finely divided state. 5.2 Sieve, with nominal apertures of 425
17、4m, complying with the requirements of BS 410. 5.3 Sieve, with nominal apertures of 250 4m, complying with the requirements of BS 410. 5.4 Analytical balance, accurate to 0.001 g. 5.5 Extraction apparatus (see Figure 1) NOTEAlternatively, it is permissible to use a Soxhlet-type apparatus, complying
18、with the requirements of BS 2071, in which the material in the thimble is surrounded by the vapour of the boiling solvent. Any other extraction apparatus may be used, provided that it can be shown to give similar results. 5.6 Oven, circulating air type, capable of being controlled at 50 2 C (see BS
19、2648). 6 Preparation of test sample Mould two discs, each of 100 mm to 130 mm diameter and 6.5 0.5 mm thickness, using the conditions specified in the relevant British Standard for the material. Reduce the mouldings to powder by any suitable means, taking care that no undue heating of the material o
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- BS 2782 METHOD 451 1978
链接地址:https://www.31doc.com/p-3731231.html