1、J IS JAPANESE INDUSTRIAL STANDARD Translated and Published by Japanese Standards Association Carbon steel pipes for high pressure service ICs 23.040.10; 77.140.75 Reference number : JIS G 3455 : 2005 (E) PROTECTED BY COPYRIGHT 14 S G 3455 : 2005 Foreword This translation has been made based on the o
2、riginal Japanese Industrial Standard revised by the Minister of Economy, Trade and Industry through deliberations at the Japanese Industrial Standards Committee, as the result of proposal for revision of Japanese Industrial Standard submitted by The Japan Iron and Steel Federation (JISF) with the dr
3、aft being attached, based on the provision of Article 12 Clause 1 of the Industrial Standardization Law applicable to the case of revision by the provision of Article 14. Consequently JIS G 3455 : 1988 is replaced with this Standard. This revision has been made based on IS0 9329-2 : 1997 Seamless st
4、eel tubes for pressure purposes-Technical delivery conditions-Part 2: Unalloyed and alloyed steels with specified elevated temperature properties for the purposes of making it easier to compare this Standard with International Standard; to prepare Japanese Industrial Standard conforming with Interna
5、tional Standard; and to propose a draft of an International Standard which is based on Japanese Industrial Standard. Attention is drawn to the possibility that some parts of this Standard may conflict with a patent right, application for a patent after opening to the public, utility model right or a
6、pplication for registration of utility model after opening to the public which have technical properties. The relevant Minister and the Japanese Industrial Standards Committee are not responsible for identifying the patent right, application for a patent after opening to the public, utility model ri
7、ght or application for registration of utility model after opening to the public which have the said technical properties. Date of Establishment: 1962-03-01 Date of Revision: 2005-03-20 Date of Public Notice in Official Gazette: 2005-03-22 Investigated by: Japanese Industrial Standards Committee Sta
8、ndards Board Technical Committee on Iron and Steel JIS G 3455 : 2005, First English edition published in 2005-09 Translated and published by: Japanese Standards Association 4-1-24, Akasaka, Minato-ku, Tokyo, 107-5440 JAPAN In the event of any doubts arising as to the contents, the original JIS is to
9、 be the final authority. O JSA 2005 All rights reserved. Unless otherwise specified, iio part of this publication may be reproduced or utilized in any forin or by any ineaiis, electronic or mechanical, includiiig photocopying and microfilm, without permission in writing from the publisher. Printed i
10、n Japan KAIAT PROTECTED BY COPYRIGHT G 3455 : 2005 Contents Page Introduction . 1 2 3 4 5 5.1 5.2 6 6.1 6.2 6.3 7 8 8.1 8.2 9 10 Scope Normative references Grade and designation . Method of manufacture Chemical composition . Ladle analysis values Product analysis Mechanical properties . Tensile stre
11、ngth. yield point or proof stress and elongation Flattening test . Bending Hydraulic test characteristic or nondestructive characteristic . Dimensions. weight and dimensional tolerances . Dimensions and weight Dimensional tolerances . Appear ance . Test 10.1 Chemical analysis 10.2 Tensile test . 10.
12、3 Flattening test . 10.4 Bending test . 10.5 Hydraulic test or nondestructive examination . 11 Inspection 11.1 Inspection 11.2 Reinspection 1 1 1 2 2 3 3 3 3 3 4 5 5 5 5 7 8 8 8 8 8 9 9 10 10 11 (i) PROTECTED BY COPYRIGHT -,-,- G 3455 : 2005 12 Marking . 11 13 Report 11 Annex 1 (normative) Supplemen
13、tary quality requirements . 12 Annex 2 (informative) Comparison table between JIS and corresponding International Standard . 14 (ii) PROTECTED BY COPYRIGHT -,-,- JAPANESE INDUSTRIAL STANDARD JIS G 3455 : 2005 Carbon steel pipes for high pressure service Introduction This Japanese Industrial Standard
14、 has been prepared based on the first edition of IS0 9329-2 Seamless steel tubes for pressure purposes-Technical delivery conditions-Part 2: Unalloyed and alloyed steels with specified elevated tem- perature properties published in 1997 with some modifications of the technical con- tents. The portio
15、ns given sidelines or dotted underlines are the matters modified from the original International Standard. A list of modifications with the explanations is given in annex 2 (informative). 1 Scope “pipes”) used for high pressure service at a maximum temperature of 350 “C. This Standard specifies the
16、carbon steel pipes (hereafter referred to as Remarks 1 With the previous agreement of the manufacturer, the purchaser may designate part or all of the supplementary quality requirements specified in annex 1, in addition to the items specified in this text. 2 The International Standard corresponding
17、to this Standard is as follows. In addition, symbols which denote the degree of correspondence in the contents between the relevant International Standard and JIS are IDT (identical), MOD (modified), and NEQ (not equivalent) ac- cording to ISO/IEC Guide 21. IS0 9329-2 : 1997 Seamless steel tubes for
18、 pressure purposes-Tech- nical delivery conditions-Part 2: Unalloyed and alloyed steels with specified elevated temperature properties (MOD) 2 Normative references The following standards contain provisions which, through reference in this text, constitute provisions of this Standard. The most recen
19、t edi- tions of the standards (including amendments) indicated below shall be applied. JIS G 0320 JIS G 0321 JIS G 0404 JIS G 0415 JIS G 0567 JIS G O582 JIS G O583 JIS Z 2201 Standard test methods for heat analysis of steel products Product analysis and its tolerance for wrought steel Steel and stee
20、l products-General technical delivery requirements Steel and steel products-Inspection documents Method of elevated temperature tensile test for steels and heat-resisting alloys Ultrasonic examination for steel pipes and tubes Eddy current examination of steel pipes and tubes by encircling coil tech
21、nique Test pieces for tensile test for metallic materials PROTECTED BY COPYRIGHT -,-,- 2 G 3455 : 2005 Designation of grade JIS Z 2241 JIS Z 2242 JIS Z 8401 Method of tensile test for metallic materials Method of impact test for metallic materials Guide to the rounding of numbers Designation of manu
22、facturing process Manufacturing process of tubes Method of finishing Marking 3 Grade and designation The pipe shall be classified into three grades and the designations of grade and manufacturing process shall be as given in table 1. Hot finished: H Cold finished: c Marking of manufacturing method s
23、hall be as i2 b). STS 370 STS 410 STS 480 Seamless: S Method of manufacture Method of manufacture shall be as follows: The pipe shall be manufactured from killed steel by the seamless process and shall be finished according to table 1. The pipe shall be subjected to the heat treatment specified in t
24、able 2. The heat treatment other than those specified in table 2 shall be agreed upon by the pur- chaser and the manufacturer. When required by the purchaser, the pipe may be furnished with a bevel end(1). Note (l) Unless otherwise specified, the shape of the bevel end shall be as shown in figure 1.
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- JIS 3455 2005 ENG
链接地址:https://www.31doc.com/p-3783188.html